Hierarchical microstructures to overcome the conflict between strength and toughness of hard coatings: TiN/Ni as a model system

Author

Ignacio Lopez Cabanas

Graduation Semester and Year

2022

Language

English

Document Type

Dissertation

Degree Name

Doctor of Philosophy in Materials Science and Engineering

Department

Materials Science and Engineering

First Advisor

Ye Cao

Abstract

In the recent times, industry's production speed has been increasing and thus, the production of parts needs to adapt and so do the materials used to manufacture them. Hence, tools exposed to more extreme conditions using hard coatings need them to be more reliable. In this work an improvement of the toughness of TiN/Ni coatings is achieved through the combination of different microstructures at different levels. This first part consisted on finding the optimum TiN/Ni composition by using a high throughput methodology for a faster analysis and the second on the combination of that composition with a multilayer structure to emulate nacre. The coatings prepared for the high throughput methodology were TiN/Ni with a Ni content ranging from 0 to 20 at.% in the same substrate by reactive magnetron sputtering with a continuous gradient. Since all the compositions were deposited under identical conditions any differences coming from deposition parameters are removed. By screening the mechanical properties, composition and microstructure it was found that TiN with around 10 at.%Ni presented the highest hardness and fracture toughness. These increments were found to be related to the formation a nanocomposite microstructure composed by equiaxed d-TiN grains surrounded by an amorphous tissue phase. The hierarchical addition of Ni first to TiN and then a multilayer system presents a similar hardness to pure TiN but much higher toughness. Analysis on the fracture mechanisms revealed that in all cases the crack propagates through the grain boundaries and particle interfaces. Additionally, the coatings were tested at 500ºC, it was found that the multilayer system with TiN(10)Ni showed a ductile behaviour while the others were brittle, which is attributed to a higher Ni volume segregated into particles.

Keywords

Hard coatings, High throughput analysis, Hardness, Fracture toughness, Residual stresses, Nacre, Hierarchical microstructure, TiN/Ni coatings

Disciplines

Engineering | Materials Science and Engineering

License

This work is licensed under a Creative Commons Attribution-NonCommercial-Share Alike 4.0 International License.

Comments

Degree granted by The University of Texas at Arlington

Recommended Citation

Lopez Cabanas, Ignacio, "Hierarchical microstructures to overcome the conflict between strength and toughness of hard coatings: TiN/Ni as a model system" (2022). Material Science and Engineering Dissertations. 97.
https://mavmatrix.uta.edu/materialscieng_dissertations/97